A series of phosphosilicates P(2)O(5) (45 mol%)-CaO (20-40 mol%)-Na(2)O (5-20 mol%)-SiO(2) (10-15 mol%) has been synthesised by the sol-gel route using PO(OH)(3-x)(OC(2)H(5))(x) (x = 1, 2) as the phosphorus precursor. Evolution of the gels with temperature was studied using thermogravimetric analysis and differential thermal analysis. These phosphosilicates show good stability against crystallisation remaining fully amorphous even after calcination at 400 degrees C. The short-range structure of the stabilised sol-gel glasses and the effect of adding modifier oxides to the network structure have been investigated using a combination of techniques: FT-IR spectroscopy, (31)P magic angle spinning NMR, high energy XRD and P L-edge XANES.

Sol-gel produced sodium calcium phosphosilicates for bioactive applications: synthesis and structural characterisation

CARTA, DANIELA;
2011-01-01

Abstract

A series of phosphosilicates P(2)O(5) (45 mol%)-CaO (20-40 mol%)-Na(2)O (5-20 mol%)-SiO(2) (10-15 mol%) has been synthesised by the sol-gel route using PO(OH)(3-x)(OC(2)H(5))(x) (x = 1, 2) as the phosphorus precursor. Evolution of the gels with temperature was studied using thermogravimetric analysis and differential thermal analysis. These phosphosilicates show good stability against crystallisation remaining fully amorphous even after calcination at 400 degrees C. The short-range structure of the stabilised sol-gel glasses and the effect of adding modifier oxides to the network structure have been investigated using a combination of techniques: FT-IR spectroscopy, (31)P magic angle spinning NMR, high energy XRD and P L-edge XANES.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11584/77970
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 11
  • ???jsp.display-item.citation.isi??? 10
social impact