The authors investigate the tetragonal(T)-orthorhombic(O) transient zone of YBa2Cu3O6+x, in a comparative way on pair samples one of which is produced by deintercalation [D] and the other by intercalation [I] of intrinsic oxygen in the basal Cu(1)Ox plane and having the same oxygen content (k) and thermal history. Resistive and electron diffraction measurements, performed on [D]k-[I]k pairs within the composition range 0.28 ≤ k ≤ 0.32, are reported. Direct evidence is provided that the T-OII transient is a structural and electronic two phase region characterized by the (T+OII)[D]0.30 non-superconducting (non-SC) and (OII+OIII*)[I]0.30 superconducting (SC) phases. The OII superstructure represents the minority component of [D]0.30 phase and the majority one of [I]0.30 and OIII* is a new orthorhombic anti-OIII superstructure. The nature of the non-SC and SC behaviours has been comparatively investigated by NQR analysis at the T-OII borderline. The evaluated different values of the average chain lengths emphasize the role of the Cu-O chain length on the hole doping efficiency in YBCO at constant oxygen content.

The Role of CuO Chain Length on Superconductivity Emergence in YBa2Cu3O6.30

SANNA, SAMUELE;
2000-01-01

Abstract

The authors investigate the tetragonal(T)-orthorhombic(O) transient zone of YBa2Cu3O6+x, in a comparative way on pair samples one of which is produced by deintercalation [D] and the other by intercalation [I] of intrinsic oxygen in the basal Cu(1)Ox plane and having the same oxygen content (k) and thermal history. Resistive and electron diffraction measurements, performed on [D]k-[I]k pairs within the composition range 0.28 ≤ k ≤ 0.32, are reported. Direct evidence is provided that the T-OII transient is a structural and electronic two phase region characterized by the (T+OII)[D]0.30 non-superconducting (non-SC) and (OII+OIII*)[I]0.30 superconducting (SC) phases. The OII superstructure represents the minority component of [D]0.30 phase and the majority one of [I]0.30 and OIII* is a new orthorhombic anti-OIII superstructure. The nature of the non-SC and SC behaviours has been comparatively investigated by NQR analysis at the T-OII borderline. The evaluated different values of the average chain lengths emphasize the role of the Cu-O chain length on the hole doping efficiency in YBCO at constant oxygen content.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11584/83773
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus ND
  • ???jsp.display-item.citation.isi??? ND
social impact