The photolummescence and electron spin resonance properties of gamma irradiated (up to 500 kGy) porous silica are reported. By exciting at 5.6 eV a photoluminescence contribution can be detected before irradiation, peaked at about 4.1 eV. Gamma irradiation causes the generation of the E' centers (about 1 x 10(14) defects cm(-3)) of paramagnetic hole centers and modifies the photoluminescence properties of the sample: the emission amplitude decreases and three contributions can be singled out at about 3.3, 3.8 and 4.4 eV. (c) 2005 Elsevier B.V. All rights reserved.
Photoluminescent and paramagnetic centers in gamma irradiated porous silica
CARBONARO, CARLO MARIA;CORPINO, RICCARDO;
2005-01-01
Abstract
The photolummescence and electron spin resonance properties of gamma irradiated (up to 500 kGy) porous silica are reported. By exciting at 5.6 eV a photoluminescence contribution can be detected before irradiation, peaked at about 4.1 eV. Gamma irradiation causes the generation of the E' centers (about 1 x 10(14) defects cm(-3)) of paramagnetic hole centers and modifies the photoluminescence properties of the sample: the emission amplitude decreases and three contributions can be singled out at about 3.3, 3.8 and 4.4 eV. (c) 2005 Elsevier B.V. All rights reserved.
I metadati presenti in IRIS UNICA sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono protetti da diritto d'autore, salvo diversa indicazione.