Enargite, a copper arsenic sulfide having the formula Cu3AsS4, is a source of arsenic and may cause environmental problems owing to the release of toxic elements upon oxidation, especially in acid mine effluents. In this work the oxidative dissolution of enargite has been studied on freshly cleaved samples exposed to distilled water, sulfuric acid solution at pH 4 and acidic FeCl3 or Fe2(SO4)3 solutions at pH ca. 2 with 0.025 M Fe3+ simulating abiotic acid mine drainage environments. The open circuit potential of the acidic solutions with ferric ions achieved stabilization at + 0.72 ± 0.02 V NHE thus, according to the mixed potential theory, the redox couple Fe3+/Fe2+ strongly polarizes the enargite surface towards positive potentials. Solution analyses showed that in these conditions about 10-14 μg copper are released every 24 h into solution from approximately 0.5 cm2 enargite surface. Based on the amount of dissolved copper, the thickness of the dissolved enargite has been calculated to be about 60-130 nm. XPS analyses of the reacted enargite surfaces revealed no changes in the binding energy of copper Cu2p3/2 found at 932.4 ± 0.2 eV, arsenic As3d5/2 found at 43.3 ± 0.2 eV and of sulfur, S2p3/2 at 161.9 ± 0.2 eV compared to the pristine surface, whereas a prominent sulfur signal appeared at ca. 163.5 ± 0.2 eV, assigned to sulfur in a copper-deficient layer. The XPS quantitative analysis performed by applying a three-layer model revealed the presence of a metal-deficient layer of ca. 0.7 nm thickness on the enargite surface. The interface beneath this layer (estimated thickness 5-10 nm) was slightly enriched in sulfur and depleted in copper. Based on these complementary data from solution analysis and XPS surface analysis, a model similar to the dissolution of binary metallic alloys is here proposed for enargite dissolution under oxidizing conditions.
Electrochemical and XPS surface analytical studies on the reactivity of enargite
ELSENER, BERNHARD;ATZEI, DAVIDE;FANTAUZZI, MARZIA;ROSSI, ANTONELLA
2007-01-01
Abstract
Enargite, a copper arsenic sulfide having the formula Cu3AsS4, is a source of arsenic and may cause environmental problems owing to the release of toxic elements upon oxidation, especially in acid mine effluents. In this work the oxidative dissolution of enargite has been studied on freshly cleaved samples exposed to distilled water, sulfuric acid solution at pH 4 and acidic FeCl3 or Fe2(SO4)3 solutions at pH ca. 2 with 0.025 M Fe3+ simulating abiotic acid mine drainage environments. The open circuit potential of the acidic solutions with ferric ions achieved stabilization at + 0.72 ± 0.02 V NHE thus, according to the mixed potential theory, the redox couple Fe3+/Fe2+ strongly polarizes the enargite surface towards positive potentials. Solution analyses showed that in these conditions about 10-14 μg copper are released every 24 h into solution from approximately 0.5 cm2 enargite surface. Based on the amount of dissolved copper, the thickness of the dissolved enargite has been calculated to be about 60-130 nm. XPS analyses of the reacted enargite surfaces revealed no changes in the binding energy of copper Cu2p3/2 found at 932.4 ± 0.2 eV, arsenic As3d5/2 found at 43.3 ± 0.2 eV and of sulfur, S2p3/2 at 161.9 ± 0.2 eV compared to the pristine surface, whereas a prominent sulfur signal appeared at ca. 163.5 ± 0.2 eV, assigned to sulfur in a copper-deficient layer. The XPS quantitative analysis performed by applying a three-layer model revealed the presence of a metal-deficient layer of ca. 0.7 nm thickness on the enargite surface. The interface beneath this layer (estimated thickness 5-10 nm) was slightly enriched in sulfur and depleted in copper. Based on these complementary data from solution analysis and XPS surface analysis, a model similar to the dissolution of binary metallic alloys is here proposed for enargite dissolution under oxidizing conditions.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.