The structural and magnetic properties of two Fe(2)O(3)-SiO(2) nanocomposites, containing respectively 16.9 and 28.5 wt.% Fe(2)O(3), were investigated. The samples were synthetized by a sol-gel method, using ethylene glycol as a solvent, and heating the gels gradually to 900 degreesC. The procedure allowed us to obtain gamma -Fe(2)O(3) nanoparticles homogeneously dispersed in the amorphous silica matrix. The particles have a narrow size distribution and mean sizes from 3 to 6 nm depending on the iron oxide content. The magnetic properties of the samples were investigated by static and dynamic susceptibility measurements. All the samples showed superparamagnetic behaviour. The superparamagnetic relaxation was investigated also by Mossbauer spectroscopy. Hysteresis loops were measured at 2.5 K and both samples showed high values of coercive field. The role of magnetic interparticle interactions on the magnetic properties is discussed.
Superparamagnetic behaviour of gamma-Fe(2)O(3) nanoparticles dispersed in a silica matrix
CANNAS, CARLA;CONCAS, GIORGIO;FALQUI, ANDREA;MUSINU, ANNA MARIA GIOVANNA;
2001-01-01
Abstract
The structural and magnetic properties of two Fe(2)O(3)-SiO(2) nanocomposites, containing respectively 16.9 and 28.5 wt.% Fe(2)O(3), were investigated. The samples were synthetized by a sol-gel method, using ethylene glycol as a solvent, and heating the gels gradually to 900 degreesC. The procedure allowed us to obtain gamma -Fe(2)O(3) nanoparticles homogeneously dispersed in the amorphous silica matrix. The particles have a narrow size distribution and mean sizes from 3 to 6 nm depending on the iron oxide content. The magnetic properties of the samples were investigated by static and dynamic susceptibility measurements. All the samples showed superparamagnetic behaviour. The superparamagnetic relaxation was investigated also by Mossbauer spectroscopy. Hysteresis loops were measured at 2.5 K and both samples showed high values of coercive field. The role of magnetic interparticle interactions on the magnetic properties is discussed.I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.