We present a study of the electrochemical oxidation process of porous silicon. We analyze the effect of the layer thickness (1.25-22 μm) and of the applied current density (1.1-11.1 mA/cm2, values calculated with reference to the external samples surface) on the oxidation process by comparing the galvanostatic electrochemical impedance spectroscopy (EIS) measurements and the optical specular reflectivity of the samples. The results of EIS were interpreted using an equivalent circuit to separate the contribution of different sample parts. A different behavior of the electrochemical oxidation process has been found for thin and thick samples: whereas for thin samples the oxidation process is univocally related to current density and thickness, for thicker samples this is no more true. Measurements by Energy Dispersive Spectroscopy using a Scanning Electron Microscopy confirmed that the inhomogeneity of the electrochemical oxidation process is increased by higher thicknesses and higher currents. A possible explanation is proposed to justify the different behavior of thin and thick samples during the electrochemical process
Electrochemical impedance spectroscopy of oxidized porous silicon
MULA, GUIDO;FALQUI, ANDREA;PALMAS, SIMONETTA;MASCIA, MICHELE
2014-01-01
Abstract
We present a study of the electrochemical oxidation process of porous silicon. We analyze the effect of the layer thickness (1.25-22 μm) and of the applied current density (1.1-11.1 mA/cm2, values calculated with reference to the external samples surface) on the oxidation process by comparing the galvanostatic electrochemical impedance spectroscopy (EIS) measurements and the optical specular reflectivity of the samples. The results of EIS were interpreted using an equivalent circuit to separate the contribution of different sample parts. A different behavior of the electrochemical oxidation process has been found for thin and thick samples: whereas for thin samples the oxidation process is univocally related to current density and thickness, for thicker samples this is no more true. Measurements by Energy Dispersive Spectroscopy using a Scanning Electron Microscopy confirmed that the inhomogeneity of the electrochemical oxidation process is increased by higher thicknesses and higher currents. A possible explanation is proposed to justify the different behavior of thin and thick samples during the electrochemical processFile | Dimensione | Formato | |
---|---|---|---|
articolopubblicato.pdf
Solo gestori archivio
Tipologia:
versione post-print (AAM)
Dimensione
1.05 MB
Formato
Adobe PDF
|
1.05 MB | Adobe PDF | Visualizza/Apri Richiedi una copia |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.