Micropatterns and nanopatterns of gold embedded in silver and titanium embedded in gold have been prepared by combining either photolithography or electron-beam lithography with a glue-free template-stripping procedure. The obtained patterned surfaces have been topographically characterized using atomic force microscopy and scanning electron microscopy, showing a very low root-mean-square roughness (<0.5 nm), high coplanarity between the two metals (maximum height difference ≈ 2 nm), and topographical continuity at the bimetallic interface. Spectroscopic characterization using X-ray photoelectron spectroscopy (XPS), time-of-flight secondary-ion mass spectrometry (ToF-SIMS), and Auger electron spectroscopy (AES) has shown a sharp chemical contrast between the two metals at the interface for titanium patterns embedded in gold, whereas diffusion of silver into gold was observed for gold patterns embedded in silver. Surface flatness combined with a high chemical contrast makes the obtained surfaces suitable for applications involving functionalization with molecules by orthogonal adsorption chemistries or for instrumental calibration. The latter possibility has been tested by determining the image sharpness and the analyzed area on circular patterns of different sizes for each of the spectroscopic techniques applied for characterization.This is the first study in which the analyzed area has been determined using XPS and AES on a flat surface, and the first example of a method for determining the analyzed area using ToF-SIMS.

Fabrication and Microscopic and Spectroscopic Characterization of Planar, Bimetallic, Micro- and Nanopatterned Surfaces

ROSSI, ANTONELLA
Secondo
;
2017-01-01

Abstract

Micropatterns and nanopatterns of gold embedded in silver and titanium embedded in gold have been prepared by combining either photolithography or electron-beam lithography with a glue-free template-stripping procedure. The obtained patterned surfaces have been topographically characterized using atomic force microscopy and scanning electron microscopy, showing a very low root-mean-square roughness (<0.5 nm), high coplanarity between the two metals (maximum height difference ≈ 2 nm), and topographical continuity at the bimetallic interface. Spectroscopic characterization using X-ray photoelectron spectroscopy (XPS), time-of-flight secondary-ion mass spectrometry (ToF-SIMS), and Auger electron spectroscopy (AES) has shown a sharp chemical contrast between the two metals at the interface for titanium patterns embedded in gold, whereas diffusion of silver into gold was observed for gold patterns embedded in silver. Surface flatness combined with a high chemical contrast makes the obtained surfaces suitable for applications involving functionalization with molecules by orthogonal adsorption chemistries or for instrumental calibration. The latter possibility has been tested by determining the image sharpness and the analyzed area on circular patterns of different sizes for each of the spectroscopic techniques applied for characterization.This is the first study in which the analyzed area has been determined using XPS and AES on a flat surface, and the first example of a method for determining the analyzed area using ToF-SIMS.
File in questo prodotto:
File Dimensione Formato  
acs.langmuir.7b00942.pdf

Solo gestori archivio

Descrizione: articolo principale
Tipologia: versione editoriale (VoR)
Dimensione 5.5 MB
Formato Adobe PDF
5.5 MB Adobe PDF   Visualizza/Apri   Richiedi una copia
la7b00942_si_001.pdf

Solo gestori archivio

Descrizione: supporting information
Tipologia: versione editoriale (VoR)
Dimensione 605.83 kB
Formato Adobe PDF
605.83 kB Adobe PDF   Visualizza/Apri   Richiedi una copia

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11584/218182
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 14
  • ???jsp.display-item.citation.isi??? 14
social impact