High-temperature plastic deformation and dynamic recrystallization of AZ31 extruded (EX) and heat treated (FA) alloy was investigated in the temperature range between 200 and 400 ◦C. High-temperature straining resulted in partial dynamic recrystallization above 250 ◦C; in the EX alloy recrystallization was complete at 300 ◦C, while a moderate grain growth was observed at 400 ◦C. The peak flow stress dependence on temperature and strain rate are described by means of the conventional sinh equation; the calculation of the activation energy for high temperature in the whole range of temperature deformation gives Q = 155 kJ/mol, i.e. a value that was reasonably close but higher than the activation energy for self diffusion in Mg. The microstructure resulting from high-temperature straining was found to be substantially different in EX and FA alloys; in particular, the EX alloy was characterized by a lower flow stress, a higher ductility and by a finer size of the dynamically recrystallized grains. These results arethen discussed on the basis of the “necklace” mechanism of dynamic recrystallization.

Analysis of high-temperature deformation and microstructure of an AZ31 magnesium alloy

EL MEHTEDI, Mohamad;
2007-01-01

Abstract

High-temperature plastic deformation and dynamic recrystallization of AZ31 extruded (EX) and heat treated (FA) alloy was investigated in the temperature range between 200 and 400 ◦C. High-temperature straining resulted in partial dynamic recrystallization above 250 ◦C; in the EX alloy recrystallization was complete at 300 ◦C, while a moderate grain growth was observed at 400 ◦C. The peak flow stress dependence on temperature and strain rate are described by means of the conventional sinh equation; the calculation of the activation energy for high temperature in the whole range of temperature deformation gives Q = 155 kJ/mol, i.e. a value that was reasonably close but higher than the activation energy for self diffusion in Mg. The microstructure resulting from high-temperature straining was found to be substantially different in EX and FA alloys; in particular, the EX alloy was characterized by a lower flow stress, a higher ductility and by a finer size of the dynamically recrystallized grains. These results arethen discussed on the basis of the “necklace” mechanism of dynamic recrystallization.
2007
Magnesium alloys; Hot deformation; Microstructure; Recrystallization
File in questo prodotto:
File Dimensione Formato  
121_MSA_AZ31.pdf

Solo gestori archivio

Descrizione: articolo online
Tipologia: versione editoriale (VoR)
Dimensione 813.04 kB
Formato Adobe PDF
813.04 kB Adobe PDF   Visualizza/Apri   Richiedi una copia

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11584/294368
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 135
  • ???jsp.display-item.citation.isi??? 123
social impact