Influence of the Spark Plasma Sintering temperature on the structure and dielectric properties of BaTi(1-x)ZrxO3 ceramics

In this work, structural and dielectric properties of BaTi(1-x)ZrxO3 (BTZ) ceramics prepared by Spark Plasma Sintering (SPS) from powders obtained via Self-propagating High-temperature Synthesis (SHS) are shown to be strongly affected by the sintering temperature. In addition, a post-annealing treatment in air of the as-prepared ceramics leads to a transition from the hexagonal to the tetragonal and cubic phases. The SPS ceramics corresponding to compositions 0.05 ≤ x ≤ 0.20 and obtained at a sintering temperature of 1200 °C exhibit a standard ferroelectric behavior. In contrast, a diffuse phase transition is observed for the case of ceramics sintered at higher temperatures. Finally, the BTZ ceramic containing 5 at.% of Zr displays the best dielectric permittivity and piezoelectric properties as compared to the other compositions taken into account.