In this study, the effect of wood powder and nanoclay particle content on composites’ mechanical behavior made with polyethylene matrix has been investigated. The wood flour as a rein-forcer made of wood powder was at levels of 30, 40, and 50 wt.%, and additional reinforcement with nanoclay at 0, 1, 3, and 5 wt.%. Furthermore, to make a composite matrix, high-density polyethylene was used at levels of 70, 60, and 50% by weight. Wood-plastic composite (WPC) specimens were manufactured in injection molding. After preparing the specimens, tensile and bending tests were performed on samples. The mechanical properties such as tensile and flexural strength and flexural modulus were measured. Results showed that nanoclay particle content increases flexural modulus, flexural strength, modulus of elasticity, and tensile strength. The experimental test results show that Young’s moduli increased with the volume of wood flour. The biggest modulus of elasticity was achieved in the samples having 50 wt.% of wood powder. Furthermore, the highest value of tensile strength was achieved at the level of 30 wt.%. The highest flexural strength was for the sample containing 50% wood powder by weight. Additionally, a numerical model was made utilizing the Abaqus software using the finite element method (FEM). Comparing the numerical and experimental results, it was found that they are compatible in the linear-elastic and plastic state of the material. There are no crucial differences between experiment and FEM.

Experimental and numerical investigation of tensile and flexural behavior of nanoclay wood-plastic composite

Eremeyev V. A.
2021-01-01

Abstract

In this study, the effect of wood powder and nanoclay particle content on composites’ mechanical behavior made with polyethylene matrix has been investigated. The wood flour as a rein-forcer made of wood powder was at levels of 30, 40, and 50 wt.%, and additional reinforcement with nanoclay at 0, 1, 3, and 5 wt.%. Furthermore, to make a composite matrix, high-density polyethylene was used at levels of 70, 60, and 50% by weight. Wood-plastic composite (WPC) specimens were manufactured in injection molding. After preparing the specimens, tensile and bending tests were performed on samples. The mechanical properties such as tensile and flexural strength and flexural modulus were measured. Results showed that nanoclay particle content increases flexural modulus, flexural strength, modulus of elasticity, and tensile strength. The experimental test results show that Young’s moduli increased with the volume of wood flour. The biggest modulus of elasticity was achieved in the samples having 50 wt.% of wood powder. Furthermore, the highest value of tensile strength was achieved at the level of 30 wt.%. The highest flexural strength was for the sample containing 50% wood powder by weight. Additionally, a numerical model was made utilizing the Abaqus software using the finite element method (FEM). Comparing the numerical and experimental results, it was found that they are compatible in the linear-elastic and plastic state of the material. There are no crucial differences between experiment and FEM.
2021
mechanical properties; nanoclay; polyethylene; wood powder; wood-plastic composite
File in questo prodotto:
File Dimensione Formato  
materials-14-02773-v3.pdf

accesso aperto

Descrizione: articolo online
Tipologia: versione editoriale (VoR)
Dimensione 1.62 MB
Formato Adobe PDF
1.62 MB Adobe PDF Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11584/321479
Citazioni
  • ???jsp.display-item.citation.pmc??? 1
  • Scopus 8
  • ???jsp.display-item.citation.isi??? 5
social impact