The selectivity of the EXAFS (extended x-ray absorption fine structure) technique was used in order to gain insights on the structural evolution of the Fe and Co environment at different stages of the preparation of FeCo-Al2O3 aerogels and xerogels. The gels, which were prepared using aluminium tri-sec-butoxide, iron nitrate and cobalt nitrates as precursors, were dried using different procedures in order to obtain xerogels and aerogels, respectively. After drying, the samples are treated either in air up to 900 degrees C or in hydrogen up to 800 degrees C.
An EXAFS study on iron-cobalt-alumina nanocomposites prepared by the sol-gel method RID F-5547-2010
CASULA, MARIA FRANCESCA;NAVARRA, GABRIELE
2005-01-01
Abstract
The selectivity of the EXAFS (extended x-ray absorption fine structure) technique was used in order to gain insights on the structural evolution of the Fe and Co environment at different stages of the preparation of FeCo-Al2O3 aerogels and xerogels. The gels, which were prepared using aluminium tri-sec-butoxide, iron nitrate and cobalt nitrates as precursors, were dried using different procedures in order to obtain xerogels and aerogels, respectively. After drying, the samples are treated either in air up to 900 degrees C or in hydrogen up to 800 degrees C.
I metadati presenti in IRIS UNICA sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono protetti da diritto d'autore, salvo diversa indicazione.