In this study, we present the preparation of superparamagnetic ordered mesoporous silica (SOMS) for biomedical applications by the combination of high energy ball milling (HEBM) and the liquid crystal template method (LCT) to produce a material comprised of room temperature superparamagnetic Fe₃O₄ nanoparticles in a MCM-41 like mesostructured silica. In a typical synthesis, a mixture of Fe₂O₃ and silica was sealed in a stainless-steel vial with steel balls. Ball milling experiments were performed in a vibratory mill apparatus. The milling process produced nanocomposites with an average size ranging from ∼100-200 nm, where the Fe₃O₄ nanoparticles (4.8 nm size) are homogeneously dispersed into the amorphous SiO₂ matrix. The obtained nanocomposite has been used for the preparation of the SOMS through the LCT method. Structural, morphological and textural characterization were performed using X-ray powder diffraction, transmission electron microscopy and nitrogen sorption analysis. Field dependence of magnetization was investigated and showed superparamagnetic behaviour at 300 K with a value of saturation magnetization (Ms) that is of interest for biomedical applications.

High Energy Ball Milling and Liquid Crystal Template Method: A Successful Combination for the Preparation of Magnetic Nano-Platforms

Scano, Alessandra
Membro del Collaboration Group
;
Pilloni, Martina
Membro del Collaboration Group
;
Peddis, Davide
Membro del Collaboration Group
;
Sini, Franca
Membro del Collaboration Group
;
Ennas, Guido
Membro del Collaboration Group
2021-01-01

Abstract

In this study, we present the preparation of superparamagnetic ordered mesoporous silica (SOMS) for biomedical applications by the combination of high energy ball milling (HEBM) and the liquid crystal template method (LCT) to produce a material comprised of room temperature superparamagnetic Fe₃O₄ nanoparticles in a MCM-41 like mesostructured silica. In a typical synthesis, a mixture of Fe₂O₃ and silica was sealed in a stainless-steel vial with steel balls. Ball milling experiments were performed in a vibratory mill apparatus. The milling process produced nanocomposites with an average size ranging from ∼100-200 nm, where the Fe₃O₄ nanoparticles (4.8 nm size) are homogeneously dispersed into the amorphous SiO₂ matrix. The obtained nanocomposite has been used for the preparation of the SOMS through the LCT method. Structural, morphological and textural characterization were performed using X-ray powder diffraction, transmission electron microscopy and nitrogen sorption analysis. Field dependence of magnetization was investigated and showed superparamagnetic behaviour at 300 K with a value of saturation magnetization (Ms) that is of interest for biomedical applications.
2021
Superparamagnetic Ordered Mesoporous Silica; Magnetite; Fe3O4/MCM-41; Embedded MCM-41
File in questo prodotto:
File Dimensione Formato  
21JNN-19041-Ennas High Energy Ball milling Magnetic Nano Platform.pdf

Solo gestori archivio

Tipologia: versione post-print (AAM)
Dimensione 768.08 kB
Formato Adobe PDF
768.08 kB Adobe PDF   Visualizza/Apri   Richiedi una copia

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11584/330740
Citazioni
  • ???jsp.display-item.citation.pmc??? 1
  • Scopus ND
  • ???jsp.display-item.citation.isi??? ND
social impact