Ac susceptibility and static magnetization measurements were performed in the optimally doped SmFeAsO0.8F0.2 superconductor. The field-temperature phase diagram of the superconducting state was drawn, and, in particular, the features of the flux lines were derived. The dependence of the intragrain depinning energy on the magnetic field intensity was derived in the thermally activated flux-creep framework, enlightening a typical 1/H dependence in the high-field regime. The intragrain critical current density was extrapolated in the zero-temperature and zero-magnetic-field limit, showing a remarkably high value Jc0(0)~2×10^7 A/cm2, which demonstrates that this material is rather interesting for potential future technological applications.

Vortex dynamics and irreversibility line in optimally doped SmFeAsO0.8F0.2 from ac susceptibility and magnetization measurements

SANNA, SAMUELE;
2011-01-01

Abstract

Ac susceptibility and static magnetization measurements were performed in the optimally doped SmFeAsO0.8F0.2 superconductor. The field-temperature phase diagram of the superconducting state was drawn, and, in particular, the features of the flux lines were derived. The dependence of the intragrain depinning energy on the magnetic field intensity was derived in the thermally activated flux-creep framework, enlightening a typical 1/H dependence in the high-field regime. The intragrain critical current density was extrapolated in the zero-temperature and zero-magnetic-field limit, showing a remarkably high value Jc0(0)~2×10^7 A/cm2, which demonstrates that this material is rather interesting for potential future technological applications.
2011
superconductivity; vortex motion; ac susceptibility
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11584/74392
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 41
  • ???jsp.display-item.citation.isi??? 39
social impact