The electrochemical performances of Co3O4 nanopowders, obtained by the sol-gel method, were investigated and compared with those of commercial Co3O4 powders, for oxygen evolution reaction in alkaline solution. The active oxide powder was mixed with teflon and assembled on Ti substrate to form thin catalyst film. Cyclic voltammetry, polarization curves, and electrochemical impedance spectroscopy were used to assess the mechanism of oxygen evolution reaction, chemical structure, and morphology of the catalyst.
Oxygen evolution on Ti/Co3O4 – coated electrodes in alkaline solution
PALMAS, SIMONETTA;FERRARA, FRANCESCA;
2007-01-01
Abstract
The electrochemical performances of Co3O4 nanopowders, obtained by the sol-gel method, were investigated and compared with those of commercial Co3O4 powders, for oxygen evolution reaction in alkaline solution. The active oxide powder was mixed with teflon and assembled on Ti substrate to form thin catalyst film. Cyclic voltammetry, polarization curves, and electrochemical impedance spectroscopy were used to assess the mechanism of oxygen evolution reaction, chemical structure, and morphology of the catalyst.
File in questo prodotto:
Non ci sono file associati a questo prodotto.
I metadati presenti in IRIS UNICA sono rilasciati con licenza Creative Commons CC0 1.0 Universal, mentre i file delle pubblicazioni sono protetti da diritto d'autore, salvo diversa indicazione.