Nanoporous spherical assemblies of iso-oriented cobalt ferrite nanoparticles with a high surface area were prepared via a normal micelles process. The spherical magnetic assemblies were coated with a silica layer through an inverse micelles route. The microstructure and morphology were studied by X-ray diffraction, transmission electron microscopy and N 2-physisorption techniques. The primary CoFe 2O 4 nanocrystalline particles (∼7 nm) assemble into spherical nanoporous aggregates with an average size of about 50-60 nm and the coating process leads to core-shell nanostructures with an amorphous 7-8 nm thick silica shell that covers the spherical assemblies homogeneously. The magnetic properties of both uncoated and silica-coated nanostructures were also investigated
Spherical nanoporous assemblies of iso-oriented cobalt ferrite nanoparticles:synthesis, microstructure and magnetic properties
CANNAS, CARLA;ARDU, ANDREA;MUSINU, ANNA MARIA GIOVANNA;PEDDIS, DAVIDE;
2008-01-01
Abstract
Nanoporous spherical assemblies of iso-oriented cobalt ferrite nanoparticles with a high surface area were prepared via a normal micelles process. The spherical magnetic assemblies were coated with a silica layer through an inverse micelles route. The microstructure and morphology were studied by X-ray diffraction, transmission electron microscopy and N 2-physisorption techniques. The primary CoFe 2O 4 nanocrystalline particles (∼7 nm) assemble into spherical nanoporous aggregates with an average size of about 50-60 nm and the coating process leads to core-shell nanostructures with an amorphous 7-8 nm thick silica shell that covers the spherical assemblies homogeneously. The magnetic properties of both uncoated and silica-coated nanostructures were also investigatedI documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.