The impact response of stitched graphite/epoxy laminates was examined with the aim of evaluating the efficiency of stitching as a reinforcing mechanism able to improve the delamination resistance of laminates. The investigation, which focussed on two classes of cross-ply stacking sequences ([03/903]s and [0/90]3s), showed that the role of stitches in controlling damage progression of laminates and their capability to reduce the impact sensitivity of specimens are greatly dependent on the impact behaviour of base (unstitched) laminates. In [03/903]s laminates, in particular, stitching is able to reduce damage area, on condition that the impact energy is higher than a threshold level and delaminations are sufficiently developed. In [0/90]3s laminates, on the other hand, stress concentration regions generated by the stitching process appear to promote the initiation and propagation of fibre fractures, thereby inducing a decrease in the penetration resistance of the laminate.
Damage response of stitched cross-ply laminates under impact loadings
AYMERICH, FRANCESCO;PANI, CARLA;
2007-01-01
Abstract
The impact response of stitched graphite/epoxy laminates was examined with the aim of evaluating the efficiency of stitching as a reinforcing mechanism able to improve the delamination resistance of laminates. The investigation, which focussed on two classes of cross-ply stacking sequences ([03/903]s and [0/90]3s), showed that the role of stitches in controlling damage progression of laminates and their capability to reduce the impact sensitivity of specimens are greatly dependent on the impact behaviour of base (unstitched) laminates. In [03/903]s laminates, in particular, stitching is able to reduce damage area, on condition that the impact energy is higher than a threshold level and delaminations are sufficiently developed. In [0/90]3s laminates, on the other hand, stress concentration regions generated by the stitching process appear to promote the initiation and propagation of fibre fractures, thereby inducing a decrease in the penetration resistance of the laminate.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.