When isolated conjugated polymer (CP) chains are studied by single molecule spectroscopy, excitation power density in the range of 10-1000 W cm(-2) is normally used. We show that at such excitation power densities the fluorescence ability of CPs is significantly reduced. A new methodological approach allowed us to measure the fluorescence quantum yield (QY) of thin matrix polymer films doped with fluorophores at very low concentration using fluorescence microscopy. Fluorescence QYs of different conjugated polymers (P3HT, MEH-PPV, PFBV and cyclodextrin-coated PFBV-Rtx) and a reference perylene diimide dye dispersed in the PMMA matrix were measured as a function of the excitation power density that ranged from similar to 10(-4) to 100 W cm(-2). Already at an excitation power of 0.1 W cm(-2) (the power density of the sunlight at the Earth) a detectable reduction of the fluorescence QY was observed for most of the polymers. The origin of the QY reduction is exciton annihilation by photo-generated triplet and/or change-transfer states. Insulation by cyclodextrin was found to decrease significantly the effect of non-emissive quenching states.

When isolated conjugated polymer (CP) chains are studied by single molecule spectroscopy, excitation power density in the range of 10-1000 W cm -2 is normally used. We show that at such excitation power densities the fluorescence ability of CPs is significantly reduced. A new methodological approach allowed us to measure the fluorescence quantum yield (QY) of thin matrix polymer films doped with fluorophores at very low concentration using fluorescence microscopy. Fluorescence QYs of different conjugated polymers (P3HT, MEH-PPV, PFBV and cyclodextrin-coated PFBV-Rtx) and a reference perylene diimide dye dispersed in the PMMA matrix were measured as a function of the excitation power density that ranged from ∼10-4 to 100 W cm -2. Already at an excitation power of 0.1 W cm-2 (the power density of the sunlight at the Earth) a detectable reduction of the fluorescence QY was observed for most of the polymers. The origin of the QY reduction is exciton annihilation by photo-generated triplet and/or change-transfer states. Insulation by cyclodextrin was found to decrease significantly the effect of non-emissive quenching states. This journal is © the Partner Organisations 2014.

Photo-induced fluorescence quenching in conjugated polymers dispersed in solid matrices at low concentration

Sforazzini G
Membro del Collaboration Group
;
2014-01-01

Abstract

When isolated conjugated polymer (CP) chains are studied by single molecule spectroscopy, excitation power density in the range of 10-1000 W cm -2 is normally used. We show that at such excitation power densities the fluorescence ability of CPs is significantly reduced. A new methodological approach allowed us to measure the fluorescence quantum yield (QY) of thin matrix polymer films doped with fluorophores at very low concentration using fluorescence microscopy. Fluorescence QYs of different conjugated polymers (P3HT, MEH-PPV, PFBV and cyclodextrin-coated PFBV-Rtx) and a reference perylene diimide dye dispersed in the PMMA matrix were measured as a function of the excitation power density that ranged from ∼10-4 to 100 W cm -2. Already at an excitation power of 0.1 W cm-2 (the power density of the sunlight at the Earth) a detectable reduction of the fluorescence QY was observed for most of the polymers. The origin of the QY reduction is exciton annihilation by photo-generated triplet and/or change-transfer states. Insulation by cyclodextrin was found to decrease significantly the effect of non-emissive quenching states. This journal is © the Partner Organisations 2014.
2014
When isolated conjugated polymer (CP) chains are studied by single molecule spectroscopy, excitation power density in the range of 10-1000 W cm(-2) is normally used. We show that at such excitation power densities the fluorescence ability of CPs is significantly reduced. A new methodological approach allowed us to measure the fluorescence quantum yield (QY) of thin matrix polymer films doped with fluorophores at very low concentration using fluorescence microscopy. Fluorescence QYs of different conjugated polymers (P3HT, MEH-PPV, PFBV and cyclodextrin-coated PFBV-Rtx) and a reference perylene diimide dye dispersed in the PMMA matrix were measured as a function of the excitation power density that ranged from similar to 10(-4) to 100 W cm(-2). Already at an excitation power of 0.1 W cm(-2) (the power density of the sunlight at the Earth) a detectable reduction of the fluorescence QY was observed for most of the polymers. The origin of the QY reduction is exciton annihilation by photo-generated triplet and/or change-transfer states. Insulation by cyclodextrin was found to decrease significantly the effect of non-emissive quenching states.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11584/284107
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 25
  • ???jsp.display-item.citation.isi??? 25
social impact